Study on 3D Printing Process of Hydroxyapatite Via Digital Light Processing
GU Jiajun1, JIAO Chen1, CAO Ying1, HAN Xiao2, TIAN Zongjun1
1. College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;
2. Beijing Institute of Space Mechanics & Electricity, Beijing 100094, China
Because of its high strength, low density, high temperature resistance and corrosion resistance, ceramic materials have a broad application prospect in aerospace field. Aiming at the limitation of traditional molding method, the digital light possessing of hydroxyapatite is studied in this paper. Using micrometer hydroxyapatite powder and photo sensitive resin, the hydroxyapatite ceramic slurry for 3D printing was prepared and the hydroxyapatite ceramic blank was formed. Based on TG–DSC thermal analysis, the degreasing process parameters of ceramic green body were determined, and hydroxyapatite ceramic samples were sintered. The surface morphology of the sample was observed by SEM. The phase composition of the sample was analyzed by X-ray diffraction and the density was measured by Archimedes drainage method. The bending strength of the sample was measured by a universal material tester. The experimental results show that hydroxyapatite ceramic samples with density of 94.9% and flexural strength of 41.3MPa can be fabricated by using digital light pocessing.
引用本文:
顾嘉骏,焦晨,曹颖,韩霄,田宗军. 基于光固化的羟基磷灰石3D打印工艺研究[J]. 航空制造技术, 2019, 62(17): 68-72.
GU Jiajun, JIAO Chen, CAO Ying, HAN Xiao, TIAN Zongjun. Study on 3D Printing Process of Hydroxyapatite Via Digital Light Processing. Aeronautical Manufacturing Technology, 2019, 62(17): 68-72.