Effect of Sand Blasting Treatment on Surface State of 8Cr4Mo4V Steel
WEI Yinghua1, YUAN Xiaoguang1, AN Min2, ZHOU Chibin1, YU Xingfu1
1. School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China;
2. AECC Harbin Bearing Co., Ltd., Harbin 150500, China
8Cr4Mo4V steel is mainly used to the aero-engine bearings manufacture. The service environment is complex and the working conditions are harsh. In order to meet the requirements of fatigue performance and surface state, some parts of the bearings need sand blasting treatment. In this paper, the surface of 8Cr4Mo4V steel was sand-blasted under various conditions. The residual stress on the surface of 8Cr4Mo4V steel was measured by X-ray residual stress tester after sand blasting under various conditions. The surface morphology was observed by SEM, and the variation of dimension and surface roughness were measured after sand blasting. The results show that the residual compressive stress on the surface of 8Cr4Mo4V steel is generated by sand blasting, and the maximum residual compressive stress can reach –1576MPa. The value of residual compressive stress is proportional to the pressure and time of sand blasting, and inversely proportional to the particle size of sand. After sand blasting treatment, a compact layer was formed on the surface of 8Cr4Mo4V steel. The thickness of the compact layer was mainly affected by sand blasting pressure and increased with the sand blasting pressure raising. Sand blasting has a stripping effect on the surface layer of 8Cr4Mo4V steel. The amount of surface layer stripped increases with the increase of sand blasting pressure and time, and the decrease of sand particle size. The main factor is the sand particle size which affects the surface roughness of 8Cr4Mo4V steel after sand blasting. When the sand particle size is small, the roughness value is the lowest after sand blasting.
作者简介: 魏英华:硕士研究生,研究方向为轴承钢热处理。
引用本文:
魏英华,袁晓光,安敏,周驰滨,于兴福. 喷砂处理对8Cr4Mo4V钢表面状态的影响[J]. 航空制造技术, 2019, 62(21): 40-46.
WEI Yinghua, YUAN Xiaoguang, AN Min, ZHOU Chibin, YU Xingfu. Effect of Sand Blasting Treatment on Surface State of 8Cr4Mo4V Steel. Aeronautical Manufacturing Technology, 2019, 62(21): 40-46.