Research on Failure Behavior and Life Prediction of Thermal Barrier Coatings
SONG Jia’nan1, LI Shaolin1,2, QI Hongyu1,2, SHI Duoqi1,2, YANG Xiaoguang1,2
1. School of Energy and Power Engineering, Beihang University, Beijing 100191, China;
2. Collaborative Innovation Center of Advanced Aero-Engine, Beijing 100191, China
The thermal barrier coatings (TBCs) is an important technology for aero-engine hot components. Moreover, the strength analysis and lifetime prediction of TBCs are hot issues of basic research. During the service of hot components, the failure of TBCs will accelerate the degradation of substrate and threaten the safety of flight. The proper life model of TBCs can release the probability of failure and improve the reliability of engines. The damage mechanism of TBCs and the development of lifetime prediction were introduced. Furthermore, the development trend of thermal barrier coating life analysis technology for aero-engines was discussed.
基金资助:国家自然科学基金(2015CB057400;NSFC51571010)。
作者简介: 宋佳楠:博士研究生,主要研究方向为热障涂层- 高温合金系统的强度寿命及可靠性分析工作。
引用本文:
宋佳楠,李少林,齐红宇,石多奇,杨晓光. 热障涂层失效行为与寿命预测研究进展[J]. 航空制造技术, 2019, 62(3): 34-40.
SONG Jia’nan, LI Shaolin, QI Hongyu, SHI Duoqi, YANG Xiaoguang. Research on Failure Behavior and Life Prediction of Thermal Barrier Coatings. Aeronautical Manufacturing Technology, 2019, 62(3): 34-40.