Properties of Chopped Fiber Reinforced Polyimide Composites
ZHANG Peng1, DU Jianan2, BAO Jianwen1, ZHONG Xiangyu1, LIU Gang1, CHEN Xiangbao1
1. National Key Laboratory of Advanced Composites, AVIC Composite Technology Center, Beijing 101300, China;
2. School of Statistics, Jiangxi University of Finance and Economics, Nanchang 330013, China
The chopped fiber reinforced thermosetting polyimide composites (C–T700/HT–350RTM) were produced through molding process, and the chopped T700 carbon fiber (C–T700) were chosen as reinforcing material, the HT–350RTM polyimide were chosen as resin matrix. The influences of changing carbon fiber volume fraction on the coefficient of linear expansion and mechanical properties of C–T700/HT–350RTM composites were investigated. The experimental results showed that the coefficient of linear expansion of C–T700/HT–350RTM composites decreased with the chopped fiber volume fraction increased, and the tensile modulus, compression modulus, flexural modulus increased with increasing chopped fiber volume fraction, while the tensile strength and flexural strength first increased and then decreased, the compressive strength has slowly increased with the increasing of chopped fiber volume fraction.
作者简介: 张朋:工程师,研究方向为耐高温树脂基复合材料相关技术及应用。
引用本文:
张朋1,杜家楠2,包建文1,钟翔屿1,刘刚1,陈祥宝1. 短切碳纤维增强聚酰亚胺复合材料性能[J]. 航空制造技术, 2018, 61(14): 78-82.
ZHANG Peng1, DU Jianan2, BAO Jianwen1, ZHONG Xiangyu1, LIU Gang1, CHEN Xiangbao1. Properties of Chopped Fiber Reinforced Polyimide Composites. Aeronautical Manufacturing Technology, 2018, 61(14): 78-82.