The curing reaction kinetic parameters of CF832/T700 ultra-thin carbon fiber prepreg/epoxy resin systems were studied through DSC tests. The influence laws of pre-absorbing process parameters and curing process parameters on the mechanical properties of ultra-thin carbon fiber composite laminates were investigated by orthogonal tests. The most suitable adhesive film was determined by using three different adhesive films of EA9696NW, LWF–2B and FM73M to co-cure the ultra-thin prepreg laminates and Nomex honeycomb. The results show that the curing reaction activation energy of CF832/T700 prepregs is 85.98kJ/mol, the curing reaction is a slow first-order reaction. The pre-curing temperature, curing temperature and post-curing temperature are 115℃ , 135℃ and 171℃ , respectively. The bending and stretching experiments were carried out with the orthogonal analysis, the best pre-absorbing and curing process parameters are obtained, including pre-absorbing temperature 60℃ , pre-absorbing pressure magnitude 0.3MPa and pre-absorbing time 10min. The best curing parameters of curing temperature, curing pressure and curing time are 130℃, 0.4MPa and 2.5h. The EA9696NW adhesive film presents the best co-curing performance.