球头铣刀结构参数对钛合金铣削表面完整性的影响
任军学，姚倡锋，田卫军，梁永收，杨碧琦
西北工业大学
Effect of Ball-End Milling Structural Parameters on Surface Integrity for Titanium Alloy Milling
摘要 针对硬质合金球头铣刀铣削钛合金TC17，研究了不同刀具结构参数对表面粗糙度、表面形貌、残余应力和微观组织的影响。结果表明：刀具参数选择前角 γ 0 =8°，后角 α 0 =12°，螺旋角 β=35°，可获得最好的表面完整性，表面粗糙度为 0.40µm，x 向残余压应力为 324MPa，y 向残余压应力为 218MPa，表层组织无明显变化。
关键词 ：
钛合金 ,
表面完整性 ,
刀具结构参数
Abstract ：Aiming at milling TC17 titanium alloy materials with carbide ball-end mill, effects of different ball-end cutter structural parameters on surface roughness, surface morphology, residual stress and micro-organizations are studied. The results show that when the rake γ 0=8°, fl ank α 0 =12° and helix angle β=35°, the best surface integrity for test pieces can be obtained. The surface roughness is about 0.40μm, the residual compressive stress in x direction is 324MPa, the residual compressive stress in y direction is 218MPa. And surface integrity doesn’t obriously change.
Key words ：
Titanium alloy
Surface integrity
Structural parameters of ball-end milling
基金资助: 国 家 自 然 科 学 基 金（50975237）、国 家 科 技 重 大 专 项（2009ZX04014-053）、国家科技支撑计划（2008BAF32B10）、西北工业大学科技创新基金（2008KJ02018）、教育部重大项目（309026）资助项目。
[1]
刘宇，王天姝，苏全宁，马付建，杨大鹏，张生芳. 钛合金表面电火花沉积 NiCr–3 涂层的试验研究
[2]
杨圣昆，谢印开，胡全栋，李怀学. 拼接顺序对双激光选区熔化成形 TC4 钛合金成形性的影响
[3]
肖贵坚，陈树林，李少川，陈本强，卓晓琴，黄云. 磨粒磨损对砂带磨削 TC17 表面完整性的影响研究
[4]
王欣，罗学昆，宇波，汤智慧 . 航空航天用钛合金表面工程技术研究进展
[5]
孟宪凯，张正烨，周建忠，杨祥伟，冷旭忞. 激光喷丸强化 TC6 钛合金的振动疲劳寿命及断口形貌分析
[6]
张桂冠，孙玉利，范武林，王燎原，杨范轩，盛一，卢文壮，左敦稳. 钛合金加工表面完整性的研究现状与展望
[7]
杨海波，朱波，高兴强，雷羽 . 含通孔损伤变截面钛合金蜂窝壁板拉伸性能研究
[8]
谢乐春，刘兵亮，孙轩，毕健，郭豪杰，韩远飞，王立强，吕维洁. 激光熔化沉积钛合金及其复合材料组织力学性能研究进展
[9]
兰亮，白澄岩，高双，何博，王江. 电子束熔化成形 Ti–6Al–4V 钛合金研究进展和应用现状
[10]
陈哲铭，孙剑飞，朱卫东，梁培新. 置氢对 TA15 钛合金的变形及切削机理影响
[11]
张萍，李立航. 激光选区熔化成形 TC4 钛合金的电子束焊接气孔缺陷控制研究
[12]
卓义民，陈远航，杨春利. 航空发动机叶片焊接修复技术的研究现状及展望
[13]
史文祥，章文亮，陈明和，谢兰生，王宁. TB8 钛合金复杂外形桨叶前缘蒙皮多步热成形工艺研究
[14]
高宾华，保文成，陈超群，金滩，尚振涛. 延塑性航空合金磨削砂轮粘附及粘附抑制技术的研究现状与展望
[15]
黄小康，任绪凯，陈华斌，王浩，陈小奇. 高温合金机器人柔性磨削表面完整性研究进展
2010, 