| Research on Oxide Layer on Titanium Alloy Surface Treated by Electropulsing-Assisted Ultrasonic Rolling |
| WANG Baokun1，WANG Haoyu1,2，JI Renjie1，ZHENG Qian1，DONG Tiancong1，LIU Yonghong1 |
1. China University of Petroleum (East China), Qingdao 266580, China;
2. Qingdao Topscomm Communication Co., Ltd., Qingdao 266109, China |
|
|
|
|
Abstract In order to study the effect of electropulsing-assisted ultrasonic rolling on metal oxide layer, double annealed TC4 titanium alloy was treated in this way. The cross section metallograph, wear resistance and wear surface morphology of the treated surface were detected and analyzed by optical microscope, friction wear testing machine and electron microprobe. The results show that the surface oxide layer with the thickness of 120μm is transformed into a compact α–phase oxide layer with the thickness about 11μm after electropulsing-assisted ultrasonic rolling with the current of 400A. The friction and wear properties of the treated sample were tested and the low friction coefficient can maintain for a long time during the testing. The testing results show that the abrasion loss of treated sample is half of that of the turning sample and the wear surface is smooth. Meanwhile, the particles that adhere to the wear surface and the ploughs on the wear surface are less, which indicates that the wear resistance after treatment is greatly enhanced.
|
|
|
|
|
|
|
|
|
2021, 