Microstructure and Mechanical Properties of LFW Joint for TC4-DT Titanium Alloy
LIU Ying, ZHANG Chuanchen, ZHANG Tiancang
( Key Laboratory of Aeronautical Technology for Welding and Joining Technology,
摘要 针对飞机用典型的TC4-DT 钛合金线性摩擦焊接头，开展组织及接头的拉伸、冲击和低周疲劳等力学性能测试。结果表明：TC4-DT 钛合金线性摩擦焊接头经过700℃ + 保温3h 的热处理后，接头的室温和高温抗拉强度达到母材的97% 以上，室温和低温冲击性能略高于母材，室温低周疲劳性能与母材相当，具有良好的综合力学性能。
关键词 ：
TC4-DT 钛合金 ,
线性摩擦焊 ,
力学性能
Abstract ：The Microstructure, tensile strength, impact property and low-cycle fatigue testing properties were studied for TC4-DT liner friction welded (LFW) joint of the aircraft. Test results show that an excellent properties of weld joint can be obtained after post-weld heat treatment (temperature: 700℃ , longtime: 3h). The room and high tensile strengths of TC4-DT LFW joint can reach more than 97% of TC4-DT base metals, and the impact property of the weld joint is slightly higher than the base metal, the low-cycle fatigue property is close to the TC4-DT base metals.
Key words ：
TC4-DT titanium alloy
Linear friction welding
Mechanical property
[1]
吴国华，童鑫，眭怀明，魏广玲，肖旅. 铸造镁稀土合金研究现状及其在航空发动机领域应用展望
[2]
谢敏， 刘洋， 李瑞一， 裴训， 宋希文， 安胜利. Sm2 Zr2 O7 基热障涂层材料研究现状
[3]
马广义，刘德华，师敬桉，王儒政，牛方勇，吴东江. 电弧增材制造7075铝合金的微观组织与力学性能
[4]
龙雨，黄玮，郭兴，周桂兵，刁鹏源. 非传统激光束激光选区熔化 3D 打印的研究现状及展望
[5]
谢乐春，刘兵亮，孙轩，毕健，郭豪杰，韩远飞，王立强，吕维洁. 激光熔化沉积钛合金及其复合材料组织力学性能研究进展
[6]
刘丰刚，张文军，刘奋成，黄春平，郑海忠，郑永生. 激光增材制造低合金超高强度钢的组织与力学性能研究进展
[7]
陈仕奇，刘联平. 原始粉末粒度对 GH4169 合金选区激光熔化成形件组织和性能的影响
[8]
邓琳蔚，普远瞩，张少秋，杨恒，韩妙玲. 自动铺丝加热均匀性及其对复合材料性能的影响
[9]
张婷，黄爱华，李向前. 褶皱缺陷的检测及对力学性能的影响研究
[10]
耿培皓，秦国梁. 线性摩擦焊接热力耦合行为及其研究现状
[11]
车倩颖，李会霞，贺卫卫，朱纪磊，陈睿，程康康，金园园，王宇. TiAl 合金粉床电子束选区熔化成形研究进展
[12]
朱言言，李冲，刘玉婷，田象军. 复合制造 TC4 钛合金组织与拉伸性能
[13]
明越科，王奔，周晋，辛志博，李婷，王枫，段玉岗. 基于3D 打印的连续纤维增强热固性复合材料性能及其应用探索
[14]
王郁，王俊升，薛程鹏，王硕，陈东旭，张弛. 微合金化对铝合金高温析出相影响的研究进展
[15]
孟祥晨，曹炳琪，李玉龙，谷晨，万龙，黄永宪. 聚合物与铝合金特异性材料搅拌摩擦焊
2017, 