用于钛合金防微动磨损的干膜润滑剂性能研究
卢建红,王彦,岭王静,陈礼顺
中国人民解放军第五七一三厂
Properties Research of Solid Film Lubricant for Preventing Titanium Alloy From Fretting Wear
摘要 研究了干膜润滑的耐磨性、耐高温性、耐温度交变性、耐油性等性能，并与银镀层的摩擦磨损性能进行了对比研究。结果表明，干膜润滑剂具有低磨损量和摩擦系数，有较好的耐磨性，耐高温性、耐温度交变性、耐油性、失重等性能也较好。是一种综合性能优良的润滑减摩镀层。
关键词 ：
钛合金 ,
微动磨损 ,
干膜润滑剂
Abstract ：The properties of solid film hbri·cant including resistance of wear，high temperature，temperature alternating and oil are researched and compared with the friction wear properties of silver coating．Experiments indicate that the graphite solid film lubricant has less wear value and lower friction CO．efficient，has good properties of resistance of wear，high temperature，temperature alternating and oil，and has loss weight properties．Therefore，the lubricant possess-es excellent lubricating and reducing friction properties．
Key words ：
Titanium alloy ;Fretting wear
Solid film lubricant
[1]
赵冰，杨毅，李志强，慕延宏，刘胜京，张斌，张超，孙朝阳，刘杨，王新筑，褚兴荣，韩数. 钛合金空心点阵超塑成形/ 扩散连接成形工艺和性能研究
[2]
范荣磊，武永，吴迪鹏，邱佳阳，陈明和. TA32 钛合金板材的超塑胀形性能研究
[3]
彭鹏，刘太盈，蒋少松，侯晨睿，张晋源，李阳，杨尚，韩聪，卢振. TA15 钛合金局部减重中空双层结构超塑成形/ 扩散连接工艺
[4]
张晋源，秦立东，刘太盈，蒋少松，彭鹏，李阳. TA15 钛合金超薄中空四层结构超塑成形/ 扩散连接一体化成形及精度控制
[5]
王佳佳， 斌，袁臣虎，于爱兵，张文武. 钛合金水助激光打孔试验研究
[6]
刘运玺，杨毅，黄涛，周琳，陈玮，李志强，张晨辉. 固溶时效处理对新型超高强钛合金组织和力学性能的影响
[7]
王大月，顾静怡，徐雁斌，胡静. 热氧化对TA18 钛合金耐腐蚀磨损性能的影响
[8]
周丽娜，付明杰，李晓华，韩秀全. TA32 高温钛合金超塑性能研究
[9]
付余，丁悦，王腾飞，李浩，郭飞燕. 钛合金低频振动制孔切屑形态表征方法研究
[10]
冯平法，刘嘉辉，王子标，冯峰，张翔宇，沈岳，张建富，王健健，吴志军，郁鼎文. 钛合金TB6 连接孔挤压强化残余应力及疲劳寿命试验研究
[11]
李紫杨，吴松全，杨义，王皞，黄爱军. 激光选区熔化TC4 合金在HF–H2O2 体系的化学抛光研究
[12]
吴鸿燕，陈炯，桑玉蕊，陈玉华，王理涛. 工艺参数对TiNi 合金/TC4 钛合金超声波焊焊接接头形貌和力学性能的影响研究
[13]
张智鑫，樊江昆，李瑞锋，唐斌，王俭，李金山. 钛合金板材制备技术的现状及展望（上）——薄板制备技术
[14]
魏颖，房晓龙，曲宁松. TB2 钛合金电化学机械抛光试验研究
[15]
张俊杰，刘英想，胡王杰，杜鹏飞，韩腊，邓杰，邱旭，赵学森，胡振江，孙涛. TC4 钛合金纵弯超声振动铣削装置及其加工性能研究
2009, 