铝合金时效蠕变与时效应力松弛关系研究
黄晓婧，王俊彪，张贤杰
西北工业大学现代设计与集成制造技术教育部重点实验室
Research on Relationship Between Agling Creep and Stress Relaxation of Al-Alloy
摘要 分析了材料蠕变与应力松弛的关系，提出了一种由材料蠕变曲线获取应力松弛曲线的转换方法。以铝合金 7075T6 为试验材料在 177℃时效温度下实施了蠕变与应力松弛试验，通过比较试验应力松弛曲线与此转换方法得到的应力松弛曲线，验证了转换方法的准确性。
关键词 ：
时效 ,
蠕变 ,
应力松弛 ,
铝合金
Abstract ：A theoretical method for obtaining stress relaxation curve from creep curve is proposed in this paper. This method is based on the analysis of relationship between creep and stress relaxation. In order to verify the theoretical model, creep and stress relaxation experiments at 177 ℃ on 7075T6 aluminum alloy are performed, and results are compared with those predicted by the model for stress relaxation. Good agreements between the model predictions and the experiment results are found.
Key words ：
Aging
Creep
Stress relaxation
Alu-minum alloy
基金资助: 陕西省“13115”科技创新工程重大科技专项（2007ZDKG-65）资助项目。
[1]
孟祥晨，王伟，谢聿铭，董继红，夏佩云，黄永宪. 7075–T6铝合金随焊碾压搅拌摩擦焊接头变形控制和性能评价
[2]
许飞，高文强，刘斌，雷鹏程，闫晓锋. 7050–T7451高强铝合金激光电弧复合焊缝横截面几何形状与组织性能的相关性
[3]
陈超，高义皓，任柏桥，隋昕晨，傅彦. 铝合金激光–电弧复合焊接技术的研究进展
[4]
黄晓龙，罗灿，张臣. 薄壁5A06铝合金双缝T型接头振荡激光–电弧复合焊接数值模拟研究
[5]
施渊吉，潘超，夏腾飞，郭训忠，陈泽瑜. AA5052铝合金管材自由弯曲成形起皱缺陷预测的研究
[6]
陈程，刘天奇，陈晨忻，郭瑾，葛爽，李晨. 陶瓷颗粒增强铝合金材料疲劳性能研究
[7]
冯义成，王凤春，张祥斌，王雷，马宝霞，李瑞珩. 7065铝合金厚板的组织与力学性能研究
[8]
倪世东，王勇超，黄庆奕，蔡杨，谢延敏. 基于改进J–C本构模型的6061铝合金薄壁件温热成形工艺参数优化
[9]
杨丰，慕延宏，杜立华. TA32钛合金应力松弛行为及热成形回弹预测
[10]
沈炜智，牛秋林，荆露，刘俐鹏，王星华，戴福朋. 基于微量润滑的Al–60% Si合金铣削性能试验研究
[11]
田志杰，孙宇明，杜晗，米海明，郝双喜. 薄板5B70铝合金TIG焊接接头组织与性能
[12]
李荣昊，路永新，王大锋，王世清，申志康，强伟. 高强铝合金激光电弧复合焊温度场与流场研究
[13]
田子航，孙博宇，金丹，乔红超，闵业钊. 激光冲击强化对TC11钛合金应力松弛特性的影响
[14]
曲海涛，陈福龙，何宗仁，石佳瑷，韩玉杰，曹宏东，郑菁桦. 双级时效处理对2219铝合金力学性能与微观沉淀析出的影响研究
[15]
高秋阁，张立强，杨杰，钱栊. 基于ABAQUS镜像铣削铝合金表面残余应力有限元分析
2011, 