Research on Process Technology of CICC Superconductive Conductor Crust
摘要 通过焊接参数的选定（焊接电流 I ＝150A，电压 U ＝ 8.8V，焊接速度 0.7~1m/min），保证单根导体长度不小于 300m，焊缝无气孔，裂纹等焊接缺陷。使焊接后的 CICC 超导导体内部最接近焊缝位置的温度低于 183℃，确保导体导电性能，导体焊缝耐压试验不低于 5MPa，且氦气密性能良好，研制出的产品满足相关技术标准的质量要求。
关键词 ：
CICC 超导导 ,
焊接 ,
焊缝
Abstract ：Better weld quality is received by choosing technical parameter of weld (weld current is 150A, weld voltage is 8.8V, weld speed is 0.7~1.0 m/min). There is no pore and flaw in weld seam of the product, the temperature of proximal weld seam in welded CICC conduct is less than 183℃， so the electric is better. Compression resistance of weld seam is more than 5 MPa, and airproof capability is better. Product can meet demands of specifi cation.
Key words ：
CICC superconductive conductor
Welding
Weld seam
[1]
蔡得涛，罗子艺，张屹，刘伟清. 工艺参数对钛合金激光–等离子电弧同轴复合焊接的电弧电压的影响
[2]
孟祥晨，王伟，谢聿铭，董继红，夏佩云，黄永宪. 7075–T6铝合金随焊碾压搅拌摩擦焊接头变形控制和性能评价
[3]
许飞，高文强，刘斌，雷鹏程，闫晓锋. 7050–T7451高强铝合金激光电弧复合焊缝横截面几何形状与组织性能的相关性
[4]
陈超，高义皓，任柏桥，隋昕晨，傅彦. 铝合金激光–电弧复合焊接技术的研究进展
[5]
黄晓龙，罗灿，张臣. 薄壁5A06铝合金双缝T型接头振荡激光–电弧复合焊接数值模拟研究
[6]
马超，刘云浩，李鹏，夏佩云，赵艳秋，占小红. 送丝速度对镁合金激光–MIG复合焊接过程熔滴过渡行为的影响研究
[7]
丁一，董吉义，李明洋，彭祺擘，董为，吴冬梅，高永卓. 火箭燃料贮箱零件焊接前处理机器人自动打磨技术研究
[8]
戴晟. 航空热塑性复合材料焊接技术研究及应用进展
[9]
刘宝明，李卓丞，尹海军，韩志仁. 航空导管焊接工装快速设计
[10]
田志杰，孙宇明，杜晗，米海明，郝双喜. 薄板5B70铝合金TIG焊接接头组织与性能
[11]
吴迪，岳喜山，权银洙，高兴强，常川川，黄孟成. 扩散焊工艺参数对Ti2 AlNb焊接接头组织性能与变形的影响
[12]
刘小刚，朱品舟，吕浩，余嘉伟，汪全中，艾兴. 1Cr11Ni2W2MoV氩弧焊接头裂纹扩展行为及寿命预测研究
[13]
强伟，吴思晨，曹龙，彭勇，路浩，路永新，高倩，王世清. Mg–Li合金超薄板脉冲激光焊接组织及性能研究
[14]
付鹏飞，唐振云，李立航，耿康，毛智勇，赵桐. 大厚度TC4合金熔池导流电子束焊接成形
[15]
刘正尧，罗怡，王晓东，钱志龙. 精密加速度计组件自动装配及焊接系统
2011, 