超声喷丸强化搅拌摩擦焊接接头性能
张新华1 ，曾元松1 ，王东坡2
1.北京航空制造工程研究所；2.天津大学材料科学与工程学院
Properties of Friction Stir Welding Joint by Ultrasonic Shot Peening
摘要 用超声喷丸焊后处理工艺分别对 7075-T651 铝合金母材及搅拌摩擦焊焊接接头进行了处理，并与其原始状态进行了疲劳对比试验。对比疲劳性能试验结果证明该处理技术可用于提高 7075 - T651 铝合金母材及搅拌摩擦焊焊接焊接接头试件的疲劳性能。
关键词 ：
超声喷丸 ,
7075-T651铝合金 ,
搅拌摩擦 ,
焊焊接接头 ,
疲劳性能
Abstract ：The processing of hardening effectiveness by ultrasonic shot peening is used to deal with base metals of 7075 - T651 aluminum alloy and joint of friction stir welding, and is then compared with its original condition in fatigue comparative test. The result of the test of fatigue property shows that ultrasonic shot peening is available for improving the fatigue property of base metals of 7075 - T651 aluminum alloy and specimen of friction stir welding joint.
Key words ：
Ultrasonic shot peening
7075-T651 aluminum alloy
Joint of friction stir welding
Fatigue property
[1]
孟祥晨，王伟，谢聿铭，董继红，夏佩云，黄永宪. 7075–T6铝合金随焊碾压搅拌摩擦焊接头变形控制和性能评价
[2]
陈程，刘天奇，陈晨忻，郭瑾，葛爽，李晨. 陶瓷颗粒增强铝合金材料疲劳性能研究
[3]
张廷连，袁荒. 激光重熔镍基高温合金非均质材料性能研究
[4]
林伟，邱建平，史建猛，周莹，郝浩杰，张斌. 芯杆齐平度偏差对抽芯铆钉力学性能影响及机理分析
[5]
窦振，张安峰，王豫跃，黄胜，吴梦杰，王普强. 不同热处理工艺对选区激光熔化TC4动载性能及各向异性的影响
[6]
陈琨，冯振宇，马佳威，张宏宇，陈向明. 激光选区熔化成形Al–Mg–Sc–Zr合金孔隙缺陷对疲劳寿命的影响
[7]
张华，李志航，郝云飞，季亚娟，陈敏，陶虎威，姜炳鑫. 2219铝合金中厚板双轴肩搅拌摩擦焊接头析出相分布特征及耐腐蚀性能研究
[8]
郭瑞鹏，程敏，卢正冠，徐磊. 粉末冶金TC11钛合金的热等静压制备与高周疲劳性能研究
[9]
李文亚，唐益爽，邹阳帆，王卫兵. 协同双面搅拌摩擦焊接技术
[10]
邢宇辉，崔 丽，付雪松，刘标，彭晧云，陈国清，周文龙. 喷丸强化覆铝7B04–T7451铝合金的表面完整性及疲劳性能研究
[11]
陈书锦，张帅，张荣洲，李志豪，李沫琦，刘建华. 外部能场辅助搅拌摩擦焊接技术综述
[12]
倪雁冰，刘武，高康歌，赵慧慧，董吉义，孟少飞，肖聚亮，刘海涛. 双机镜像搅拌摩擦焊顶锻力变化规律与影响因素研究
[13]
黄永德，伍大为，张泽龙，刘强，陈宜. 钛合金搅拌摩擦焊搅拌头磨损机理及其涂层强化
[14]
高嵩，吴程浩，石磊，刘涛，景元坤，尹启朋，郭宁. 铝/ 钢异种金属搅拌摩擦焊性能改善方法及其研究现状
[15]
李家辰，黄立兵，李超，张亮亮，赵强，李鹏，董红刚. CFRP/金属异质材料摩擦连接技术研究进展
2010, 