预腐蚀对 AF1410 电子束焊接头疲劳性能的影响
余伟，韩鹏，吴冰
北京航空制造工程研究所高能束流加工技术重点实验室
Influence of Pre-Corrosion on Fatigue Property of AF1410 EBW Joint
摘要 AF1410 钢是一种新型的超高强度钢，是船舶、航空飞机的重要承力构件首选材料之一。这些承力构件通常采用电子束焊接，针对这些构件服役条件的特殊性，本课题提出了盐水预腐蚀对疲劳性能影响的试验方法，验证了 AF1410 钢电子束焊接接头在特殊环境下的可靠性。测试了不同腐蚀时间、不同载荷下AF1410 钢电子束焊接接头在盐水中的腐蚀疲劳性能，对获取的大量试验数据进行了深入分析。试验结果表明，预腐蚀对 AF1410 钢电子束焊接接头的疲劳寿命有一定影响，会降低焊接构件在交变载荷下的使用寿命。
关键词 ：
AF1410钢 ,
电子束焊接 ,
预腐蚀 ,
疲劳性能
Abstract ：AF1410 steel is a new type super entension steel, which is suited to manufacture key parts of ship and aircraft. Usually, these parts are welded by electron beam welding (EBW). In order to verify the reliability of AF1410 steel EBW joint, brine pre-corrosion fatigue life detection method is introduced. After different brine corrosion time, the fatigue lifes of EBW joints of AF1410 steel are obtained under different cycle loading. Through studying these test data, it can be found that pre-corrosion will decrease the fatigue life of AF1410 steel EBW joints.
Key words ：
AF1410 steel
EBW
Pre-corrosion
Fatigue property
[1]
付鹏飞，唐振云，李立航，耿康，毛智勇，赵桐. 大厚度TC4合金熔池导流电子束焊接成形
[2]
耿康，徐明，刘昕，付鹏飞，李立航，唐振云. TB18 钛合金电子束焊接接头微观组织及力学性能研究
[3]
刘颖，张世伟，周坤，张博贤，杨朝曦. 刷式密封结构GH4169+Haynes214电子束焊接组织及密封性能研究
[4]
张颖云，胡生双，朱增辉，郑超，龙健，张林杰 . 30CrMnSiNi2A 钢电子束焊接头的疲劳裂纹扩展特性研究
[5]
隋楠，周毅，张明达，曹京霞，黄旭. Ti6242钛合金电子束焊接接头组织和力学性能
[6]
张萍，李立航. 激光选区熔化成形TC4钛合金的电子束焊接气孔缺陷控制研究
[7]
司青润，董全林，桑兴华. 100kV 焊接用电子枪的设计和优化
[8]
朱军，郭顺，彭勇，周琦，王克鸿. 钛/铜电子束偏置焊接模拟及力学性能研究
[9]
曲树平，许海鹰，王晓军，桑兴华. 铝钛异种合金电子束焊接接头组织与界面分析
[10]
赵桐, 李晋炜, 唐振云, 吴冰. ZTC4合金电子束焊接接头显微组织及力学性能研究
[11]
吴爱萍，李艳军，赵玥，李权，朱瑞灿，刘磊，邹贵生，王国庆. Ti2AlNb合金电子束焊接接头的残余应力与再热裂纹
[12]
杨震，刘方军，张伟. 电子枪静电透镜部件仿真与优化
[13]
庄明祥1，李小曼1，徐 梅1，张兵宪1，杨海欧2. 30CrMnSiNi2A 超高强度钢真空电子束焊接工艺应用研究
[14]
旷小聪1,2，卜文德1，付鹏飞2，王西昌2，柯黎明1. TA15 钛合金电子束焊缝形貌及其组织研究*
[15]
关 峰1，倪家强1，刘广鑫2，侯 琦1，刘艳梅1，赵泓博1. 大厚度TC4-DT 钛合金电子束焊接接头微观组织和力学性能研究
2010, 