Effect of Ball-End Milling Structural Parameters on Surface Integrity for Titanium Alloy Milling
摘要 针对硬质合金球头铣刀铣削钛合金TC17，研究了不同刀具结构参数对表面粗糙度、表面形貌、残余应力和微观组织的影响。结果表明：刀具参数选择前角 γ 0 =8°，后角 α 0 =12°，螺旋角 β=35°，可获得最好的表面完整性，表面粗糙度为 0.40µm，x 向残余压应力为 324MPa，y 向残余压应力为 218MPa，表层组织无明显变化。
关键词 ：
钛合金 ,
表面完整性 ,
刀具结构参数
Abstract ：Aiming at milling TC17 titanium alloy materials with carbide ball-end mill, effects of different ball-end cutter structural parameters on surface roughness, surface morphology, residual stress and micro-organizations are studied. The results show that when the rake γ 0=8°, fl ank α 0 =12° and helix angle β=35°, the best surface integrity for test pieces can be obtained. The surface roughness is about 0.40μm, the residual compressive stress in x direction is 324MPa, the residual compressive stress in y direction is 218MPa. And surface integrity doesn’t obriously change.
Key words ：
Titanium alloy
Surface integrity
Structural parameters of ball-end milling
基金资助: 国 家 自 然 科 学 基 金（50975237）、国 家 科 技 重 大 专 项（2009ZX04014-053）、国家科技支撑计划（2008BAF32B10）、西北工业大学科技创新基金（2008KJ02018）、教育部重大项目（309026）资助项目。
[1]
蔡得涛，罗子艺，张屹，刘伟清. 工艺参数对钛合金激光–等离子电弧同轴复合焊接的电弧电压的影响
[2]
李宁，孙进，岳常迪，陈琳，葛世伟，王兆强，唐臣升. TA18钛合金管材数控弯曲成形研究
[3]
张鹏飞，张林嘉，周瑜，孙峰，王军，李金山. 钛合金精密铸造技术在航空航天领域的应用进展
[4]
雷奕文，贺文勃，张骞文，李细锋. 钛合金蜂窝芯瓦楞板精密成形技术研究进展
[5]
郭建烨，毛怡颖，高诗诗，侯宁. 面向薄壁件变形控制的高速铣削残余应力分析与工艺优化
[6]
杨丰，慕延宏，杜立华. TA32钛合金应力松弛行为及热成形回弹预测
[7]
卢立成，李军利，刘钢，安庆龙. 用于钛合金深腔加工的复合减振刀杆研究
[8]
梁忠伟，林子顺，唐荟，李天羿，张宇鹏，BALIGASIMA Patrick. TC11钛合金表面TiN颗粒强化层组织与性能分析
[9]
柴东升，王焕臣，刘振扬，肖贵坚. 机器人砂带磨削增材钛合金空心构件的材料去除行为及表面完整性研究
[10]
潘峰，王涛，贾东旭，马国佳，刘星，崔向中，张昊泽. 钛合金“基体效应”对WC掺杂类金刚石碳涂层力学和摩擦磨损性能的影响
[11]
田子航，孙博宇，金丹，乔红超，闵业钊. 激光冲击强化对TC11钛合金应力松弛特性的影响
[12]
马芳薇，闵祥禄，韩巍，梁巧云，袁沛雨，谭靓. K417G铸造高温合金喷丸强化表面完整性试验研究
[13]
蔡高参，胡宇恒，刘辉，汪小康，彭凯. 支柱尺寸对钛合金点阵结构薄壁件温度变化和残余应力的影响
[14]
潘妃，王宁，朱贤皓，武秋宇，张显程，陆体文，周留成，潘鑫磊. 激光冲击、喷丸及其复合强化对TC4钛合金高周疲劳性能的影响
[15]
付鹏飞，唐振云，李立航，耿康，毛智勇，赵桐. 大厚度TC4合金熔池导流电子束焊接成形
2010, 